Interfacial microstructure and mechanical properties of Ti3SiC2 ceramic and TC11 alloy joint diffusion bonded with a Cu interlayer

Reliable joints of Ti₃SiC₂ ceramic and TC11 alloy were diffusion bonded with a 50 μm thick Cu interlayer. The typical interfacial structure of the diffusion boned joint, which was dependent on the interdiffusion and chemical reactions between Al, Si and Ti atoms from the base materials and Cu interlayer, was TC11/α-Ti + β-Ti + Ti₂Cu + TiCu/Ti₅Si₄ + TiSiCu/Cu(s, s)/Ti₃SiC₂. The influence of bonding temperature and time on the interfacial structure and mechanical properties of Ti₃SiC₂/Cu/TC11 joint was analyzed. With the increase of bonding temperature and time, the joint shear strength was gradually increased due to enhanced atomic diffusion. However, the thickness of Ti₅Si₄ and TiSiCu layers with high microhardness increased for a long holding time, resulting in the reduction of bonding strength. The maximum shear strength of 251 ± 6 MPa was obtained for the joint diffusion bonded at 850 °C for 60 min, and fracture primarily occurred at the diffusion layer adjacent to the Ti₃SiC₂ substrate. This work provided an economical and convenient solution for broadening the engineering application of Ti₃SiC₂ ceramic.     

APP软件性能效率研究

性能效率是APP软件的重要质量属性，但目前缺乏APP软件性能效率的通用模型。分析了APP软件的性能特征，基于ISO/IEC 25010标准提出了APP软件的性能效率模型，定义了APP软件性能效率的子特性和度量指标。基于提出的APP软件性能效率模型，通过实验对APP软件的性能效率进行了度量及相关分析。     

激光立体成形TC4钛合金的热力场演化

激光立体成形能够实现高性能复杂零件的精确成形，但成形过程中的高温度梯度极易导致残余应力和变形，最终影响构件的几何精度和力学性能。通过搭建基板单边夹持原位热变形测量系统，探究了多道多层TC4钛合金成形件在激光立体成形过程中基板温度、变形的演化规律，分析了不同扫描策略对构件热应力场的影响。研究结果表明，构件的变形发展受其热历史驱使，扫描策略对成形件的热变形具有显著影响。     

TC4合金表面Cu/石墨复合镀层的摩擦磨损行为

采用无氰电镀工艺在TC4合金表面制备了Cu/石墨复合镀层，研究了镀层的组织结构和摩擦磨损行为。结果表明，采用无氰电镀方法能够在TC4合金表面制备出组织致密且与基体结合紧密的Cu/石墨复合镀层，但增加镀层中石墨的含量会降低镀层与基体合金的结合强度，并导致硬度小幅下降。摩擦磨损实验结果表明，Cu/石墨复合镀层具有优良的摩擦磨损防护性能，归因于石墨有效降低了镀层的摩擦系数和磨损率；对镀层磨损形貌、磨损产物和摩擦系数的综合分析结果表明，纯铜镀层的摩擦磨损机制主要为犁削磨损、黏着磨损和剥层磨损，Cu/石墨复合镀层的磨损机制为轻微的削层磨损和疲劳磨损。     

Impact of the solidification path of FeOx–SiO2 slags on the resultant inorganic polymers

Aiming to reduce the carbon dioxide emissions associated with cement production, alternative binders such as inorganic polymers currently receive substantial attention and slags from the non-ferrous metallurgy are promising precursors. However, studies  that correlate their chemistry and crystallinity with the newly formed binder remain limited. In this work, the effect of three different solidification methods on glass formation and reactivity of FeO_x–SiO₂ slags, as well as on the molecular structure of the resultant Fe-rich inorganic polymers, was investigated. The inorganic polymers were synthesized by mixing the slags (approximate molar ratio FeO/SiO₂ = 1.6) with an alkali silicate solution (molar ratios SiO₂/Na₂O = 1.6 and H₂O/Na₂O = 25). Results demonstrated that higher cooling rates promoted higher glass formation and faster reaction kinetics when the slags were activated. ⁵⁷Fe Mössbauer spectroscopy indicated that all the slags consisted predominantly of Fe²⁺ ions with a minor amount of Fe³⁺ ions, regardless of the variability in glass content. The binder phase of all inorganic polymers consisted of iron in both Fe²⁺ and Fe³⁺ states, after 28 days of curing. After pulverizing the inorganic polymer pastes and exposing the powder to air for 28 additional days, the Fe²⁺ state in the binder transformed to Fe³⁺. The compressive strength evolution of the three slags showed that the 2-day strength was higher for the samples with a higher amorphous fraction, while after 28 days, this influence was less pronounced.     

热处理工艺对TC4钛合金冲击磨损性能的影响

研究了退火和固溶时效处理对热轧态TC4钛合金的力学性能和组织的影响,并考察了其冲击磨损性能。结果表明:退火处理后试样组织中转变β相增加,强度、塑性和韧性均较热轧态有所提升;而固溶时效处理后试样组织的晶粒细化且尺寸更为均匀,同时具有最高的强度,而塑性和韧性则较热轧态有所降低。经过10 h的冲击磨损试验后,退火态试样的磨损率最低,而固溶时效态试样的磨损率最高。通过磨损断口观察发现退火态试样表面冲刷犁沟较短,且终点处存在合金的塑性堆积,同时磨损面组织发生塑性变形,晶粒延展拉长。退火态试样较高的塑性和韧性有助于吸收冲击能量,因此表现出较好的耐冲击磨损性能。     

冲击载荷下TC18钛合金力学性能模拟研究

TC18钛合金在退火状态下的屈服强度非常高,进行动态力学性能测试存在一定困难,可优先考虑采用数值模拟方法对其动态力学性能进行研究,而数值模拟结果的精确性主要取决于合金本构方程的精确性。为了减少数值模拟与实验结果之间的差异,在Johnson-Cook模型的基础上做了调整,利用ABAQUS软件的子程序接口自定义了材料本构子程序UMAT,以代码的形式来扩展ABAQUS程序的功能。通过与ABAQUS/Standard软件分析结果以及实验结果的对比,验证了自定义材料本构子程序UMAT计算结果的精确性与可靠性。该研究可为TC18钛合金的结构设计提供参考。     

退火温度对EB熔炼低成本TC4钛合金宽厚板组织和性能的影响

采用EB炉一次熔炼TC4合金扁锭作为直轧坯料,在4200 mm宽厚板轧机上成功制备出规格46 mm×2650 mm×8700 mm的低成本TC4合金宽厚板,研究了退火温度对低成本TC4合金板材显微组织和力学性能的影响。结果表明:EB熔炼TC4合金扁锭经过两火换向轧制,粗大铸态组织得到充分破碎,热轧态TC4合金板材显微组织中等轴α或条状α含量较高,横纵向室温拉伸性能差异小,横向室温冲击吸收能量小于纵向,横纵向心部强度均高于表层。TC4合金板材经750~900 ℃退火,横纵截面为等轴组织,经950 ℃退火,横纵截面为双态组织,经980 ℃退火,横截面为双态组织,纵截面为魏氏组织。随着退火温度升高,TC4合金板材抗拉强度和规定塑性延伸强度呈下降趋势,伸长率基本不变,室温冲击吸收能量先升高后降低,900 ℃退火后,强度、伸长率和冲击吸收能量达到最佳匹配。     

Trajectories of knowledge economy in SSA and MENA countries

In the first critical assessment of knowledge economy dynamic paths in Africa and the Middle East, but for a few exceptions, we find overwhelming support for diminishing cross-country disparities in knowledge-based economy dimensions. The paper employs all the four components of the World Bank's Knowledge Economy Index (KEI): economic incentives, innovation, education, and information infrastructure. The main finding suggests that sub-Saharan African (SSA) and the Middle East and North African (MENA) countries with low levels of KE dynamics and catching-up their counterparts of higher KE levels. We provide the speeds of integration and time necessary to achieve full (100%) integration. Policy implications are also discussed.